Détails sur le produit:
|
Matériau: | St35.8, St45.8, ST52,15Mo3, 13CrMo44, 10CrMo91 | la norme: | DIN17175, DIN2391 |
---|---|---|---|
Type: | Transparente | OD: | 6mm~88.9mm |
Épaisseur de paroi: | 0.8mm~15mm | Application: | CHAUDIÈRE |
Traitement de surface: | Vernis, Huile-immersion, passivation, phosphatant, grenaillage | Statut de la livraison: | Recuit, normalisé, normalized+Tempered, etc. |
Surligner: | tube sans couture d'acier au carbone,tuyaux sans couture d'acier au carbone |
Tuyauterie sans couture DIN17175 ST45.8 de chaudière d'acier au carbone tubes de chaudière à haute pression de 38,1 * 2,5 millimètres SA213 SA210
Norme de produit : GB3087, GB5310, ASME SA210, ASME SA213, DIN17175
Catégories en acier principales : 10,20,20G, 20MnG, 25MnG, 15CrMoG, 12Cr2MoG, 12Cr1MoVG, 12Cr2MoWVTiB, 10Cr9Mo1VNb, Ⅲ de SA210A1, de SA210C, de SA213 T11, de SA213 T12, de SA213 T22, de SA213 T23, de SA213 T91, de SA213 T92, de ST45.8/, 15Mo3,13CrMo44,10CrMo910 etc.
Application : Pour le waterwall de chaudière, l'économiseur, le réchauffeur et la fabrication de tuyauterie de vapeur
Conditions chimiques et propriétés mécaniques :
Standard | Catégorie | Composition chimique (%) | ||||||||||||||
C | SI | Manganèse | P | S | Cr | MOIS | Cu | Ni | V | Al | W | Ti | NOTA: | N | ||
GB3087 | 10 | 0.07~0.13 | 0.17~0.37 | 0.38~0.65 | ≤0.030 | ≤0.030 | 0.3~0.65 | / | ≤0.25 | ≤0.30 | / | / | ||||
20 | 0.17~0.23 | 0.17~0.37 | 0.38~0.65 | ≤0.030 | ≤0.030 | 0.3~0.65 | / | ≤0.25 | ≤0.30 | / | / | |||||
GB5310 | 20G | 0.17~0.24 | 0.17~0.37 | 0.35~0.65 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | |||||
20MnG | 0.17~0.24 | 0.17~0.37 | 0.70~1.00 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | ||||||
25MnG | 0.18~0.24 | 0.17~0.37 | 0.80~1.10 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | ||||||
15CrMo | 0.12~0.18 | 0.17~0.37 | 0.40~0.70 | ≤0.030 | ≤0.030 | 0.80~1.10 | 0.40~0.55 | ≤0.20 | ≤0.30 | |||||||
12Cr2MoG | 0.08~0.15 | ≤0.50 | 0.40~0.70 | ≤0.030 | ≤0.030 | 2.00~2.50 | 0.90~1.20 | ≤0.20 | ≤0.30 | |||||||
12Cr1MoV | 0.08~0.15 | 0.17~0.37 | 0.40~0.70 | ≤0.030 | ≤0.030 | 0.90~1.20 | 0.25~0.35 | ≤0.20 | ≤0.30 | 0.15~0.30 | ||||||
12Cr2MoWVTiB | 0.08~0.15 | 0.45~0.75 | 0.45~0.65 | ≤0.030 | ≤0.030 | 1.60~2.10 | 0.50~0.65 | ≤0.20 | ≤0.30 | 0.28~0.42 | 0.30~0.55 | 0.08~0.15 | B 0.002~0.008 | |||
10Cr9Mo1VNb | 0.08~0.12 | 0.20~0.50 | 0.30~0.60 | ≤0.020 | ≤0.010 | 8.00~9.50 | 0.85~1.05 | ≤0.20 | ≤0.40 | 0.18~0.25 | ≤0.015 | 0.06~0.10 | 0.03~0.07 | |||
ASME SA210 | SA210A-1 | 0.13~0.19 | ≥0.1 | 0.45~0.65 | ≤0.030 | ≤0.030 | ||||||||||
SA210C | 0.18~0.24 | ≥0.1 | 0.80~1.10 | ≤0.030 | ≤0.030 | |||||||||||
ASME SA213 | SA213 T11 | 0.05~0.15 | 0.50~1.0 | 0.30~0.60 | ≤0.030 | ≤0.030 | 1.00~1.50 | 0.50~1.00 | ||||||||
SA213 T12 | 0.05~0.15 | ≤0.50 | 0.30~0.61 | ≤0.030 | ≤0.030 | 0.80~1.25 | 0.44~0.65 | |||||||||
SA213 T22 | 0.05~0.15 | ≤0.50 | 0.30~0.60 | ≤0.030 | ≤0.010 | 1.90~2.60 | 0.87~1.13 | |||||||||
SA213 T23 | 0.04~0.10 | ≤0.50 | 0.10~0.60 | ≤0.030 | ≤0.030 | 1.90~2.60 | 0.05~0.30 | ≤0.030 | 1.45~1.75 | B0.0005~0.006 | 0.02~0.08 | ≤0.040 | ||||
SA213 T91 | 0.08~0.12 | 0.20~0.50 | 0.30~0.60 | ≤0.020 | ≤0.010 | 8.00~9.50 | 0.85~1.05 | ≤0.40 | 0.18~0.25 | ≤0.015 | 0.06~0.10 | 0.03~0.07 | ||||
SA213 T92 | 0.07~0.13 | ≤0.50 | 0.30~0.60 | ≤0.020 | ≤0.010 | 8.50~9.50 | 0.30~0.60 | ≤0.40 | 0.15~0.25 | ≤0.015 | 1.50~2.00 | B 0.001~0.006 | 0.04~0.09 | 0.03~0.07 | ||
DIN 17175 | Ⅲ de ST45.8/ | ≤0.21 | 0.10~0.35 | 0.40~1.20 | ≤0.040 | ≤0.040 | ||||||||||
15Mo3 | 0.12~0.20 | 0.10~0.35 | 0.40~0.80 | ≤0.035 | ≤0.035 | 0.25~0.35 | ||||||||||
13CrMo44 | 0.10~0.18 | 0.10~0.35 | 0.40~0.70 | ≤0.035 | ≤0.035 | 0.70~1.10 | 0.45~0.65 | |||||||||
10CrMo910 | 0.08~0.15 | ≤0.50 | 0.30~0.70 | ≤0.025 | ≤0.020 | 2.00~2.50 | 0.90~1.10 | ≤0.30 | ≤0.30 | ≤0.015 |
Standard | Catégorie | SOLIDES TOTAUX (MPA) | YS (MPA) | Élongation (%) | Dureté |
GB3087 | 10 | 335~475 | ≥195 | ≥24 | / |
20 | 410~550 | ≥245 | ≥20 | / | |
GB5310 | 20G | 410~550 | ≥245 | ≥24 | / |
20MnG | ≥415 | ≥240 | ≥22 | / | |
25MnG | ≥485 | ≥275 | ≥20 | / | |
15CrMoG | 440~640 | ≥235 | ≥21 | / | |
12Cr2MoG | 450~600 | ≥280 | ≥20 | / | |
12Cr1MoVG | 470~640 | ≥255 | ≥21 | / | |
12Cr2MoWVTiB | 540~735 | ≥345 | ≥18 | / | |
10Cr9Mo1VNb | ≥585 | ≥415 | ≥20 | / | |
ASME SA210 | SA210A-1 | ≥415 | ≥255 | ≥30 | ≤143HB |
SA210C | ≥485 | ≥275 | ≥30 | ≤179HB | |
ASME SA213 | SA213 T11 | ≥415 | ≥205 | ≥30 | ≤163HB |
SA213 T12 | ≥415 | ≥220 | ≥30 | ≤163HB | |
SA213 T22 | ≥415 | ≥205 | ≥30 | ≤163HB | |
SA213 T23 | ≥510 | ≥400 | ≥20 | ≤220HB | |
SA213 T91 | ≥585 | ≥415 | ≥20 | ≤250HB | |
SA213 T92 | ≥620 | ≥440 | ≥20 | ≤250HB | |
DIN17175 | Ⅲ de ST45.8/ | 410~530 | ≥255 | ≥21 | / |
15Mo3 | 450~600 | ≥270 | ≥22 | / | |
13CrMo44 | 440~590 | ≥290 | ≥22 | / | |
10CrMo910 | 480~630 | ≥280 | ≥20 | / |
Inspection et essai : essai de composition chimique, essai de propriétés mécaniques (de tension, rendement, élongation), essai de processus d'essai de propriétés (aplatissement, évaser, se plier, dureté, impact, etc.), d'aspect et de taille, essai d'inspection non destructive, essai hydrostastic.
Statut de la livraison : Recuit, normalisé, normalized+Tempered, etc.
Préparation de surface : grenaillage etc. d'imprégnation d'huile, de peinture, de passivation, de phosphatage.
Emballage : Exportation de la condition de /as de paquet/boîte en bois.
Marque : Au besoin.
Personne à contacter: Mrs. Yana Dong
Téléphone: 13661003712, 86-10-5712 1108, 5718 5998
Télécopieur: 86-10-56752778